Irsyadi, Akhdan Habib (2023) STUDI KOMPARASI KETAHANAN KOROSI BAJA S45C DENGAN BAJA PADUAN AISI 4340 HASIL PROSES VARIASI TEMPERATUR PLASMA NITRIDING. Sarjana (S1) thesis, Universitas Islam "45" Bekasi.
![[img]](http://repository.unismabekasi.ac.id/style/images/fileicons/text.png) |
Text
Pendahuluan.pdf Download (2MB) |
|
Text
BAB I.pdf Restricted to Repository staff only Download (26kB) | Request a copy |
|
Text
BAB II.pdf Restricted to Repository staff only Download (622kB) | Request a copy |
|
Text
BAB III.pdf Restricted to Repository staff only Download (294kB) | Request a copy |
|
Text
BAB IV.pdf Restricted to Repository staff only Download (394kB) | Request a copy |
|
Text
BAB V.pdf Restricted to Repository staff only Download (7kB) | Request a copy |
|
Text
DAFTAR PUSTAKA.pdf Download (73kB) |
Abstract
The research was carried out a comparative study of corrosion resistance of S45C and AISI 4340 materials as a result of variations in plasma nitriding temperature. Obtain the results of a comparison of corrosion resistance between S45C Steel and AISI 4340 Alloy steel. This research is expected to be useful for similar research in developing technology, especially in the field of heat treatment plasma nitriding processes. Literature study: Observing existing problems in the industry and looking for references or journals as a basis for taking titles. Material: S45C Steel and AISI 4340 Steel. Heat treatment process: Performed at PT. Kyoto Therm Indonesia. SST Test: Conducted at PT. KIRA Engineering Salt Spray Test is one of the corrosion rate tests by using a corrosive solution in a closed room so that the test object will experience corrosion in a shorter time. The research method uses temperature variations at the same time. The temperatures used were 350°C, 420°C and 500°C with a nitriding process holding time of 5 hours. Comparison results obtained from S45C Steel and AISI 4340 Steel materials from the sst test, AISI 4340 materials have a better level of corrosion resistance compared to S45C Steel. Because the value of the percentage of carats obtained is much lower than S45C Steel.
| Item Type: | Thesis (TA, Skripsi, Tesis, Disertasi) (Sarjana (S1)) | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Contributors/Dosen Pembimbing,NIDN Dosen bisa diakses di LINK https://bit.ly/NIDNdosenunismabekasi: |
|
|||||||||
| Keywords / Kata Kunci: | Heat Treatment, Plasma Nitriding, S45C Steel, AISI 4340 Steel, Corrosion | |||||||||
| Subjects: | Manufaktur | |||||||||
| Faculty: | Fakultas Teknik > Teknik Mesin S1 | |||||||||
| Depositing User: | Mr. Akhdan Habib Irsyadi | |||||||||
| Date Deposited: | 31 Aug 2023 07:35 | |||||||||
| Last Modified: | 31 Aug 2023 07:35 | |||||||||
| URI: | http://repository.unismabekasi.ac.id/id/eprint/4009 |
Actions (login required)
 |
View Item |