ANALISIS PENGARUH VARIASI TEMPERATUR HASIL PROSES PLASMA NITRIDING BAJA S45C TERHADAP KETAHANAN KOROSI

Yasa, Mahendri Cakra (2023) ANALISIS PENGARUH VARIASI TEMPERATUR HASIL PROSES PLASMA NITRIDING BAJA S45C TERHADAP KETAHANAN KOROSI. Sarjana (S1) thesis, Universitas Islam “45” Bekasi.

	Text Pendahuluan.pdf Download (5MB)
	Text bab 1.pdf Restricted to Repository staff only Download (142kB) | Request a copy
	Text bab 2.pdf Restricted to Repository staff only Download (578kB) | Request a copy
	Text bab 3.pdf Restricted to Repository staff only Download (611kB) | Request a copy
	Text bab 4.pdf Restricted to Repository staff only Download (526kB) | Request a copy
	Text bab 5.pdf Restricted to Repository staff only Download (62kB) | Request a copy
	Text daftar pustaka.pdf Download (62kB)

Abstract

ABSTRACT This research is an analysis of the effect of temperature variations resulting from the plasma nitriding process of S45C steel on corrosion resistance. The formulation of the problem that occurs is whether variations in plasma nitriding temperature parameters affect corrosion resistance and the type of corrosion that occurs. Purpose of the plasma nitriding heat treatment process is to determine the value of corrosion resistance resulting from variations in temperature of the S45C Steel material after the plasma nitriding process and the type of corrosion that occurs from differences in temperature variations of the S45C Steel material. Research related to technological developments, especially in the field of heat treatment of plasma nitriding processes and corrosion resistance processes, as well as increasing plasma nitriding knowledge and being able to determine the temperature parameters of corrosion levels due to plasma nitriding of S45C Steel material. The research method obtained was to analyze S45C steel material for corrosion resistance, the temperature used was 350 °C, 420 °C and 500 °C when removed 4, 8, 15, 21, 39, 63 and 73 hours. The conclusion is that the corrosion rate in the plasma nitriding process result of machine by four samples of S45C steel increases in direct proportion to the plasma nitriding process time and affects the rust spots. The higher the proportion of rust spots. the time and temperature of the heat treatment is directly proportional to the increase in the proportion of rust spots.